Effect of the use of bromelain associated with bioactive glass-ceramic on dentin/adhesive interface.

OBJECTIVES: To evaluate the effect of bromelain associated with Biosilicate on the bond strength (BS) of a universal adhesive system to sound (SD) and caries-affected dentin (CAD), and on the proteolytic activity. MATERIALS AND METHODS: Cavities were prepared in 360 molars, half submitted to cariogenic challenge. Teeth were separated into groups (n=20): Control-No treatment; CHX-0.12% chlorhexidine; NaOCl-5% sodium hypochlorite; Br5%-5% bromelain; Br10%-10% bromelain; Bio-10% Biosilicate; NaOClBio-NaOCl+Bio; Br5%Bio-Br5%+Bio; Br10%Bio-Br10%+Bio. Following treatments, the adhesive system was applied, and cavities were restored. Samples were sectioned into sticks and stored at 37 °C for 24 h, 6 months, and 1 year. Microtensile BS (2-way ANOVA, Bonferroni's test, α=0.05), fracture patterns (SEM), and adhesive interfaces (TEM) were evaluated. Bacterial collagenase assay and in situ zymography were performed. RESULTS: In CAD, Br10% presented higher BS (p=0.0208) than Br5%Bio. Br5% presented higher BS (p=0.0033) after 6 months than after 24 h; and association of treatments, higher BS (p<0.05) after aging than after 24 h. Mixed fractures were the most prevalent. Association of treatments promoted a more uniform hybrid layer with embedded Bio particles. Experimental groups presented lower (p<0.0001) relative fluorescence units than Control. Bromelain, associated or not with Bio, showed collagenolytic degradation. CONCLUSIONS: Bromelain associated with Biosilicate did not affect the BS to SD. In CAD, Br5%Bio decreased immediate BS but had no long-term influence. This association decreased the proteolytic activity. CLINICAL RELEVANCE: Bromelain and Biosilicate may enhance the longevity of adhesive restorations by inhibiting endogenous proteases.

Effect of epigallocatechin-3-gallate and thermal cycling on the bond strength of resin cements to the root dentin.

This study evaluated the effect of epigallocatechin-3-gallate (EGCG) solution and thermal cycling on the bond strength (BS) of fiber posts to the root dentin using two different resin cements (conventional or self-adhesive). One hundred and forty-four bovine roots were endodontically treated. After post space preparation, specimens were randomly divided into six groups (n = 24) according to dentin pretreatment [distilled water, 0.05% EGCG solution or 2% chlorhexidine (CHX) solution] and resin luting agent used for fiber post cementation (RelyX ARC or RelyX U200-3 M ESPE). Then, the samples were separated into two subgroups (n = 12): storage in distilled water at 37 °C for 24 h and thermal cycling (5 °C/55 °C, dwell time 30 s-12,000 cycles) during 6 months. After that, the specimens were subjected to the pull-out BS test (Universal Testing Machine-0.5 mm/min) and the failures pattern was analyzed in a stereomicroscope. According to the BS results (three-way ANOVA, Tukey's test, α = 0.05), the highest values were reported in the group EGCG + RelyX U200, showing significant statistical differences compared to all the other experimental groups. For Control and CHX groups BS values, there was no significant difference (p > .05) between the resin cements. For conventional resin cement, there was no significant difference among treatment solutions (p > .05). The thermal cycling did not influence the BS results (p > .05). As reported by the failure mode analysis, adhesive failure was predominant in all groups. EGCG solution improved the bond strength of self-adhesive resin cement to root dentin.

Effect of thermo-mechanical cycling and chlorhexidine on the bond strength of universal adhesive system to dentin.

OBJECTIVES: This study evaluated the influence of thermo-mechanical cycling (TMC) on the bond strength (BS) of a universal adhesive system (UAS - Adper Single Bond Universal, 3M ESPE) to dentin treated or not with 0.2% chlorhexidine (CHX). METHODS: Eighty human molars were flattened until reach the dentin and separated into 4 groups according to the bonding protocol: ENR Group: 37% phosphoric acid + 3-step etch-and-rinse adhesive system (ENR); UAS Group: UAS in self-etch mode; ENR + CHX Group: 37% phosphoric acid + CHX + ENR; UAS + CHX Group: CHX + UAS in self-etch mode. After treatments, teeth were restored (Filtek Z350, 3M ESPE). Samples (n = 10) were submitted to aging process: stored in distilled water at 37°C/30 days or TMC (ERIOS - 98N/1.6Hz + thermal cycling 5/37/55 °C - 1,200,000 cycles). Specimens were sectioned into sticks (1.0 mm2) and submitted to the microtensile test (Mechanical Test Machine - 0.5 mm/min). Fracture patterns and hybrid layer integrity were analyzed under Stereomicroscope and Scanning Electron Microscopy (SEM). RESULTS: The BS results (3-way ANOVA, Bonferroni's test, α = 5%) showed that groups treated with CHX presented higher BS values than control groups; significant in all cases (p < .05), except for ENR submitted to TMC (p > .05). When CHX was applied and samples were cycled, UAS revealed higher BS (p < .05) than ENR. After TMC, cohesive fractures increased for UAS, regardless of CHX application. SEM analysis demonstrated different hybridization patterns for the adhesive systems tested. CONCLUSION: The performance of the universal adhesive system used in self-etch mode was better than that of the 3-step etch-and-rinse adhesive system. CLINICAL SIGNIFICANCE: Universal adhesive systems have been developed in order to simplify the dentin hybridization protocol. It is important to determine the longevity of the adhesive interface using these bonding materials after chewing.

Microtensile bond strength of silorane-based composite specific adhesive system using different bonding strategies.

OBJECTIVES: The aim of this study was to evaluate the effect of pre-etching on the bond strength of silorane-based composite specific adhesive system to dentin. MATERIALS AND METHODS: Thirty human molars were randomly divided into 5 groups according to the different bonding strategies. For teeth restored with silorane-based composite (Filtek Silorane, 3M ESPE), the specific self-etching adhesive system (Adhesive System P90, 3M ESPE) was used with and without pre-etching (Pre-etching/Silorane and Silorane groups). Teeth restored with methacrylate based-composite (Filtek Z250, 3M ESPE) were hybridized with the two-step self-etching system (Clearfil SE Bond, Kuraray), with and without pre-etching (Pre-etching/Methacrylate and Methacrylate groups), or three-step adhesive system (Adper Scotchbond Multi-Purpose, 3M ESPE) (Three-step/Methacrylate group) (n = 6). The restored teeth were sectioned into stick-shaped test specimens (1.0 × 1.0 mm), and coupled to a universal test machine (0.5 mm/min) to perform microtensile testing. RESULTS: Pre-etching/Methacrylate group presented the highest bond strength values, with significant difference from Silorane and Three-step/Methacrylate groups (p < 0.05). However, it was not significantly different from Preetching/Silorane and Methacrylate groups. CONCLUSIONS: Pre-etching increased bond strength of silorane-based composite specific adhesive system to dentin.

Color stability of modern composites subjected to different periods of accelerated artificial aging

The aim of this study was to evaluate the color stability of composites subjected to different periods of accelerated artificial aging (AAA). A polytetrafluorethylene matrix (10 x 2 mm) was used to fabricate 24 test specimens of three different composites (n=8): Tetric Ceram (Ivoclar/Vivadent); Filtek P90 and Z250 (3M ESPE), shade A3. After light activation for 20 s (FlashLite 1401), polishing and initial color readout (Spectrophotometer PCB 687; BYK Gardner), the test specimens were subjected to AAA (C-UV; Comexim), in 8-h cycles: 4 h exposure to UV-B rays at 50°C and 4 h condensation at 50°C. At the end of each cycle, color readouts were taken and the test ended when the mean value of ΔE attained a level ≥3.30. Tetric Ceram presented alteration in ΔE equal to 3.33 in the first aging cycle. For Filtek P90 and Z250, two (ΔE=3.60) and four (ΔE=3.42) AAA cycles were necessary. After each cycle, there was a reduction of luminosity in all the samples (ΔL). It was concluded that a short period of AAA was sufficient to promote clinically unacceptable color alteration in composites, and that this alteration was material-dependent.

O objetivo deste estudo foi avaliar estabilidade de cor de compósitos submetidos a diferentes períodos de envelhecimento artificial acelerado (EAA). Foram confeccionados, em matriz de teflon (10x2 mm), 24 corpos-de-prova de três compósitos (n=8): Tetric Ceram (Ivoclar/Vivadent); Filtek P90 e Z250 (3M ESPE), cor A3. Após fotoativação por 20 s (FlashLite 1401), polimento e leitura inicial de cor (espectrofotômetro PCB 687; BYK Gardner), os corpos-de-prova foram submetidos ao EAA (C-UV, Comexim), com ciclos de 8 h: 4 h de exposições a raios UV-B a 50°C e 4 h de condensação a 50°C. Ao final de cada ciclo, leituras de cor eram realizadas e quando o valor médio de ΔE atingisse índice ≥3,30, o ensaio era encerrado. Observou-se que Tetric Ceram apresentou alteração de ΔE igual a 3,33 já no primeiro ciclo de envelhecimento. Com Filtek P90 foram necessários dois ciclos de EAA (ΔE=3,60) e para Z250 quatro (ΔE=3,42). Observou-se que a cada ciclo ocorria diminuição na luminosidade de todas as amostras (ΔL). Concluiu-se que um curto período de EAA já é suficiente para que compósitos apresentem alteração de cor inaceitável clinicamente e que esta alteração é material dependente.

Influence of increment thickness on the similarity of composite shade: a pilot study.

The aim of this study was to evaluate the similarity in shade between increments of different composite thicknesses. Fifty test specimens 12 mm in diameter were fabricated and separated into five groups (n = 10) according to sample thickness: 0.5 mm, 1.0 mm, 1.5 mm, 2.0 mm, and 2.5 mm. Specimens were polished with water abrasive papers and silicone points. Next, based on the CIE L*a*b* system, test specimens were submitted to color readouts, and the values obtained for the coordinates L*, a*, and b* for each thickness were compared using one-way ANOVA and a Tukey test (P < 0.05). The results demonstrated that there was a reduction in coordinate L* as the test specimen thickness increased, with statistically significant differences (P < 0.05), except for 2.0 mm and 2.5 mm thicknesses (P > 0.05). Samples 1.5 mm thick presented less variation of a*, while a greater variation occurred for samples 2.5 mm thick, with a significant difference in comparison with the other thicknesses (P < 0.05), except for 2.0 mm (P > 0.05). Samples 0.5 mm thick presented a greater variation of b*, while the lowest variation in this coordinate occurred for samples 2.5 mm thick, which was significantly different from the other samples (P < 0.05). It was concluded that different composite thicknesses do not present similarity of color and have an influence on the final result of esthetic restorations.

Color and opacity of composites protected with surface sealants and submitted to artificial accelerated aging.

OBJECTIVES: To evaluate the color similarity, stability and opacity of composites (TPH, Charisma, and Concept, shade A2) protected with surface sealants (Fortify Plus and Biscover) and cyanoacrylate (Super Bonder). METHODS: Forty specimens of each composite were made and separated into 4 groups (n=10) according to the surface protection: GI - without sealant; GII - cyanoacrylate; GIII - Fortify Plus; GIV - Biscover. Color and opacity readings were taken before and after Artificial Acelerated Aging (AAA) and the values obtained for color stability were submitted to statistical analysis by 2-way ANOVA and Bonferroni's test (P<.05). The values acquired for color similarity were submitted to 1-way ANOVA and Tukey's test (P<.05). The specimen sufaces were compared before and after AAA using Scanning Electronic Microscopy (SEM). RESULTS: Studied composites did not present the same values for the coordinates L*, a* and b * before AAA, indicating that there was no color similarity among them. All composites presented color alteration after AAA with clinically unacceptable values. Protected groups presented lower opacity variation after AAA, in comparison with the control goup. SEM evaluation demonstrated that AAA increased the surface irregularities in all of the studied groups. CONCLUSION: Surface sealants were not effective in maintaining composite color, but were able to maintain opacity.

Color stability of modern composites subjected to different periods of accelerated artificial aging.

The aim of this study was to evaluate the color stability of composites subjected to different periods of accelerated artificial aging (AAA). A polytetrafluorethylene matrix (10 x 2 mm) was used to fabricate 24 test specimens of three different composites (n=8): Tetric Ceram (Ivoclar/Vivadent); Filtek P90 and Z250 (3M ESPE), shade A3. After light activation for 20 s (FlashLite 1401), polishing and initial color readout (Spectrophotometer PCB 687; BYK Gardner), the test specimens were subjected to AAA (C-UV; Comexim), in 8-h cycles: 4 h exposure to UV-B rays at 50°C and 4 h condensation at 50°C. At the end of each cycle, color readouts were taken and the test ended when the mean value of ΔE attained a level ≥3.30. Tetric Ceram presented alteration in ΔE equal to 3.33 in the first aging cycle. For Filtek P90 and Z250, two (ΔE=3.60) and four (ΔE=3.42) AAA cycles were necessary. After each cycle, there was a reduction of luminosity in all the samples (ΔL). It was concluded that a short period of AAA was sufficient to promote clinically unacceptable color alteration in composites, and that this alteration was material-dependent.